电邮这篇文章 Fabrication of optical Yb: YAG ceramics by pressure slip casting method with subsequent vibro-impact effect
- 作者: Kozlova S.M.1, Lopukhin K.V.1, Balashov V.V.1, Listkov T.V.1, Efimov A.A.1
-
隶属关系:
- Fryazino Branch of the Kotelnikov Institute of Radioengineering and Electronics RAS
- 期: 卷 70, 编号 10 (2025)
- 页面: 997-1000
- 栏目: TO THE 70th ANNIVERSARY OF THE KOTELNIKOV IRE RAS
- URL: https://stomuniver.ru/0033-8494/article/view/696911
- DOI: https://doi.org/10.7868/S3034590125100149
- ID: 696911
如何引用文章
开放存取
##reader.subscriptionAccessGranted##
订阅或者付费存取
详细
Yb: YAG ceramic samples with a thickness of 7 mm and more were manufactured using pressure slip casting method. The samples were obtained by solid-phase synthesis using commercially available Al2O3, Y2O3 and Yb2O3 powders. Optical transmission spectra were recorded. It was shown that pressing with vibro-impact effect as a method of additional compaction is more preferable than simple uniaxial pressing, since it yields ceramics with higher optical quality.
作者简介
S. Kozlova
Fryazino Branch of the Kotelnikov Institute of Radioengineering and Electronics RAS
Email: offmrx@mail.ru
Vvedensky Squar., 1, Fryazino, Moscow Region, 141190 Russian Federation
K. Lopukhin
Fryazino Branch of the Kotelnikov Institute of Radioengineering and Electronics RAS
Email: offmrx@mail.ru
Vvedensky Squar., 1, Fryazino, Moscow Region, 141190 Russian Federation
V. Balashov
Fryazino Branch of the Kotelnikov Institute of Radioengineering and Electronics RAS
Email: offmrx@mail.ru
Vvedensky Squar., 1, Fryazino, Moscow Region, 141190 Russian Federation
T. Listkov
Fryazino Branch of the Kotelnikov Institute of Radioengineering and Electronics RAS
Email: offmrx@mail.ru
Vvedensky Squar., 1, Fryazino, Moscow Region, 141190 Russian Federation
A. Efimov
Fryazino Branch of the Kotelnikov Institute of Radioengineering and Electronics RAS
编辑信件的主要联系方式.
Email: offmrx@mail.ru
Vvedensky Squar., 1, Fryazino, Moscow Region, 141190 Russian Federation
参考
- Giesen A., Hügel H., Voss A. et al. // Appl. Phys. B. 1994. V. 58. № 5. P. 365.
- doi.org/10.1007/BF01081875
- Rutherford T.S., Tulloch W.M., Gustafson E.K. et al. // IEEE J. Quantum Electron. 2000. V. 36. № 2. P. 205.
- doi.org/10.1109/3.823467
- Yamamoto R.M., Parker J.M., Allen K.L. et al. // Proc. SPIE. 2007. V. 6552. P. 655205.
- doi.org/10.1117/12.720965
- Li J., Zhou J., Pan Y. et al. // J. Amer. Ceram. Soc. 2012. V. 95. № 3. P. 1029.
- doi.org/10.1111/j.1551-2916.2011.04915.x
- Zhang W., Pan Y., Zhou J. et al. // J. Amer. Ceram. Soc. 2009. V. 92. № 10. P. 2434.
- doi.org/10.1111/j.1551-2916.2009.03220.x
- Zhang W.X., Zhou J., Liu W.B. et al. // J. Alloys Compound. 2010. V. 506. № 2. P. 745.
- doi.org/10.1016/j.jallcom.2010.07.059
- Caslavsky J.L., Viechnicki D.J. // J. Mater. Sci. 1980. V. 15. № 7. P. 1709.
- doi.org/10.1007/BF00550589
- Ikesue A., Aung Y.L., Taira T. et al.//Annual Rev. Mater. Res. 2006. V. 36. № 1. P. 397.
- doi.org/10.1146/annurev.matsci.36.011205.152926
- Innerhofer E., Südmeyer T., Brunner F. et al. // Opt. Lett. 2003. V. 28. № 5. P. 367.
- doi.org/10.1364/OL.28.000367
- Latham W.P., Lobad A., Newell T.C. et al. // AIP Conf. Proc. 2010. V. 1278. № 1. P. 758.
- Boulesteix R., Goldstein A., Perrière C. et al. // J. Europ. Ceram. Soc. 2021. V. 41. № 3. P. 2085.
- doi.org/10.1016/j.jeurceramsoc.2020.11.003
- Xu Y., Mao X., Fan J. et al. // Ceram. Int. 2017. V. 43. № 12. P. 8839.
- doi.org/10.1016/j.ceramint.2017.04.017
- Sanghera J., Kim W., Villalobos G. et al. // Materials. 2012. V. 5. № 2. P. 258.
- doi.org/10.3390/ma5020258
补充文件